Anggraeni, Yani (2017) Pengaruh zinc nitrate tetrahydrate dan film PLA/Cu2O terhadap performa nanogenerator ZnO nanorods / Yani Anggraeni. Diploma thesis, Universitas Negeri Malang.
Full text not available from this repository.Abstract
ABSTRAK Anggraeni Yani. 2017. Pengaruh Zinc Nitrate Tetrahydrate dan Film PLA/Cu2O terhadap Performa Nanogenerator ZnO Nanorods. Skripsi Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Negeri Malang. Pembimbing (I) Nandang Mufti M.T. Ph.D (II) Dr. Ahmad Taufiq M.Si. Kata Kunci ZnO nanorods PolyLacticAcid (PLA) Piezoelektrik nanogenerator Stainless steel. ABSTRAK ZnO nanorods dapat digunakan sebagai piezoelektrik nanogenerator untuk energy harvesting. Tujuan dalam penelitian ini untuk mengoptimasi pembentukan film piezoelektrik nanogenerator berbasis ZnO nanorods dalam menghasilkan arus dan tegangan. ZnO nanorods (NRs) disintesis menggunakan metode hidrotermal pada substrat stainless steel pada suhu 90oC selama 6 jam dengan variasi konsentrasi ZnO(NO3)2.4H2O yang digunakan yaitu 50 mM 70 mM dan 90 mM. Sedangkan Hexamethylenetetramine (HMT) 35 mM dibuat tetap. Stainless steel yang lain dilapisi PLA dan PLA/Cu2O dengan menggunakan spin coating dengan kecepatan 3000 rpm selama 20 detik. ZnO nanorods yang dihasilkan kemudian dianalisis dengan XRD SEM dan nanogenerator dibuat ukuran 1 x 2 cm2. Sedangkan uji performa nanogenerator dilakukan dengan memberi gaya tekan 6 N/m2 pada film ZnO NRs PLA dan PLA/Cu2O kemudian arus dan tegangan diukur menggunakan elektrometer dan osiloskop. Dari hasil XRD diperoleh ZnO nanorods yang dihasilkan mempunyai struktur kristal hexagonal wurtzite dengan parameter kisi a b 3 2413 dan c 5 1954. Sedangkan diameter ZnO nanorods dari hasil SEM berturut-turut adalah 81 56 nm 115 8 nm dan 80 42 nm. Sedangkan panjang rod masing-masing 386 6 nm 774 0 nm dan 339 9 nm. Hasil performa nanogenerator menunjukan arus dan tegangan optimal sebesar 85 nA dan 2 2 V ketika pressing nanogenerator dengan jari/tangan. Anggraeni Yani. 2017. The Effect of Zinc Nitrate Tetrahydrate and PLA/Cu2O Films on the Performance of ZnO Nanorods Nanogenerator. Thesis Departement of Physics Faculty of Mathematics and Natural Sciences State University of Malang. Advisors (I) Nandang Mufti M.T. Ph.D (II) Dr. Ahmad Taufiq M.Si. Key words ZnO nanorods PolyLacticAcid (PLA) Piezoelectric Nanogenerator Stainless steel. Abstract ZnO nanorods can be used as piezoelectric nanogenerators for energy harvesting. The purpose of this research is to optimize the formation of nanogenerator piezoelectric film based on ZnO nanorods in generating current and voltage. ZnO nanorods (NRs) were synthesized using a hydrothermal method on a stainless steel substrate at a temperature of 90oC for 6 hours with a variation of ZnO (NO3)2.4H2O concentration used at 50 mM 70 mM and 90 mM. While Hexamethylenetetramine (HMT) 35 mM made fixed. Other stainless steel coated PLA and PLA / Cu2O using the spin coating with speed 3000 rpm for 20 seconds. The resulting ZnO nanorods were then analyzed by XRD SEM and nanogenerator 1 x 2 cm2. While the performance test of nanogenerator is done by giving force 6 N/m2 on film ZnO NRs PLA and PLA / Cu2O then current and the voltage measured using electrometer and oscilloscope. From XRD results obtained ZnO nanorods produced has a hexagonal wurtzite crystal structure with lattice parameters a b 3 2413 and c 5 1954. While the diameter of ZnO nanorods from SEM results was 81 56 nm 115 8 nm and 80 42 nm respectively. While the rod length of each 386 6 nm 774 0 nm and 339 9 nm. The nanogenerator performance results show optimum current and voltage of 85 nA and 2 2 V when pressing nanogenerator with finger/hand.
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | Q Science > QC Physics |
| Divisions: | Fakultas Matematika dan IPA (FMIPA) > Departemen Fisika (FIS) > S1 Fisika |
| Depositing User: | library UM |
| Date Deposited: | 19 Oct 2017 04:29 |
| Last Modified: | 09 Sep 2017 03:00 |
| URI: | http://repository.um.ac.id/id/eprint/20881 |
Actions (login required)
 |
View Item |