Uji kuat tekan beton ringan dengan pemakaian foam agent dan variasi volume batu apung / Sari Fatmawati - Repositori Universitas Negeri Malang

Uji kuat tekan beton ringan dengan pemakaian foam agent dan variasi volume batu apung / Sari Fatmawati

Fatmawati, Sari (2017) Uji kuat tekan beton ringan dengan pemakaian foam agent dan variasi volume batu apung / Sari Fatmawati. Diploma thesis, Universitas Negeri Malang.

Full text not available from this repository.

Abstract

ABSTRAK Fatmawati Sari. 2017. Uji Kuat Tekan Beton Ringan dengan Pemakaian Foam Agent dan Variasi Volume Batu Apung . Skripsi Program Studi S1 Teknik Sipil Fakultas Teknik Universitas Negeri Malang. Pembimbing (I) Dr. Karyadi M.P. M.T (II) Dr. Nidyawati S.T. M.T. Kata kunci Batu Apung Foam Agent Beton Ringan Kuat Tekan Modulus Elastisitas Dalam perkembangannya banyak ditemukan beton baru hasil modifikasi diantaranya yaitu beton ringan. Beton ringan sangat cocok untuk daerah yang memiliki tingkat gempa yang relatif tinggi karena berat jenis yang lebih kecil dari beton biasa sehingga dapat mengurangi berat strukturnya. Dalam penelitian ini ada dua jenis agregat yang diringankan yaitu matrik dengan penambahan foam agent tipe GF 1420 sebanyak 0 8 lt/m3 dan agregat kasar dengan menggunakan batu apung. Penelitian ini bertujuan untuk mengetahui nilai berat volume penyerapan air kuat tekan dan modulus elastisitas beton ringan dengan variasi volume batu apung campuran perbandingan 1 2 3 1 2 4 dan 1 2 5 satuan volume. Metode penelitian ini menggunakan penelitian eksperimental berupa pengujian bahan yang dilakukan di Laboraorium Bahan dan Laboratorium Struktur Jurusan Teknik Sipil Universitas Negeri Malang. Pengujian berat volume dan penyerapan air menggunakan alat timbangan digital dengan kapasitas 30 Kg dan ketelitian 0 1 g sedangkan penelitian kuat tekan dan modulus elastisitas menggunakan mesin UTM (Universal Testing Machine) dengan maksimal kekuatan 1000 kN dan ketelitian 0 1 kN. Data hasil penelitian tersebut diolah dengan menggunakan program bantu microsoft excel dan uji anova one way. Hasil penelitian terdiri dari berat volume penyerapan air kuat tekan dan modulus elastisitas. Dari ketiga jenis perlakuan masing-masing di dapatkan hasil penelitian diantaranya pada perbandingan 1 2 3 berat volume sebesar 1574 kg/m3 penyerapan air sebesar 15 07% kuat tekan sebesar 9 39 MPa dan modulus elastisitas sebesar 7910 70 MPa pada perbandingan 1 2 4 berat volume sebesar 1510 kg/m3 penyerapan air sebesar 10 96% kuat tekan sebesar 7 45 MPa dan modulus elastisitas sebesar 6631 13 MPa dan pada perbandingan 1 2 5 berat volume sebesar 1415 kg/m3 penyerapan air sebesar 13 43% kuat tekan sebesar 7 24 MPa dan modulus elastisitas sebesar 6064 76 MPa. Hasil penelitian tertinggi terdapat pada beton ringan dengan perbandingan 1 2 3. ABSTRACT Fatmawati Sari. 2017. Lightweight Concrete compressive strength with the use of Foam Agent and Volume Variation of Pumice. Under Graduate Thesis Study Program S1 Civil Engineering Faculty of Engineering State University of Malang. Advisor (I) Dr. Karyadi M.P. M.T (II) Dr. Nidyawati S.T. M.T. Keywords Pumice Foam Agent Lightweight Concrete Strong Press Modulus of Elasticity In its development many newly discovered concrete modifications include lightweight concrete. Lightweight concrete is particularly suitable for areas with relatively high earthquake levels due to density smaller than ordinary concrete thus reducing the weight of the structure. In this study there are two types of aggregates that are lightened by the matrix with the addition of foam agent type GF 1420 of 0.8 Lt / m3 and rough aggregate by using a pumice stone. This study aims to determine the value of volume weight water absorption compressive strength and modulus of lightweight concrete elasticity with a variation of pumice volume of 1 2 3 1 2 4 and 1 2 5 volume ratio. This research method uses experimental research in the form of material testing conducted in Laboratory Material and Laboratory Structure Department of Civil Engineering State University of Malang. Heavy volume and water absorption test using a digital weighing device with 30 Kg capacity and 0.1 g accuracy while compressive strength and elasticity modulus research using UTM (Universal Testing Machine) machine with maximum strength of 1000 kN and 0.1 kN accuracy. The result data is processed by using Microsoft excel program and one way another test. The results consist of volume weight water absorption compressive strength and elastic modulus. Of the three treatment types each of the results obtained in the study of the ratio of 1 2 3 volume weight of 1574 kg / m3 water absorption of 15.07% compressive strength of 9.39 MPa and elastic modulus of 7910.70 MPa At a ratio of 1 2 4 volume weight of 1510 kg / m3 water absorption of 10.96% compressive strength of 7.45 MPa and modulus of elasticity of 6631.13 MPa and at a ratio of 1 2 5 volume weight of 1415 Kg / m3 water absorption of 13.43% compressive strength of 7.24 MPa and modulus of elasticity of 6064 76 MPa. The highest research results were found in light concrete with a ratio of 1 2 3.

Item Type: Thesis (Diploma)
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Divisions: Fakultas Teknik (FT) > Departemen Teknik Sipil (TS) > S1 Teknik Sipil
Depositing User: Users 2 not found.
Date Deposited: 13 Sep 2017 04:29
Last Modified: 09 Sep 2017 03:00
URI: http://repository.um.ac.id/id/eprint/45365

Actions (login required)

View Item View Item