Sasongko, Muhammad Ilman Nur (2017) Karakterissasi fasa dan morfologi serbuk nano manganese oxide (MaO) dengan variasi sintering time / Muhammad Ilman Nur Sasongko. Diploma thesis, Universitas Negeri Malang.
Full text not available from this repository.Abstract
ABSTRAK Sasongko Muhammad Ilman Nur. 2017. Karakterisasi Fasa dan Morfologi Serbuk Nano Manganese Oxide (MnO) Dengan Variasi Sintering Time. Skripsi Program Studi Pendidikan Teknik Mesin Jurusan Teknik Mesin Fakultas Teknik Universitas Negeri Malang. Pembimbing (1) Rr. Poppy Puspitasari S.Pd. M.T. Ph.D. (2) Widiyanti. Hj. Dr. M.Pd. Kata Kunci Fasa Manganese Oxide MnO Morfologi Sintesis Sol-gel Sintering time Manganese oxide (MnO) banyak terdapat pada salah satu jenis batuan dan dapat berbentuk mineral. MnO memiliki kekurangan yaitu sangat reaktif tergolong jenis oksidator berbahaya dan dapat meledak apabila berada pada suhu diatas 55 C. Tetapi MnO memiliki sifat magnetik sifat elektrokimia dan sifat konduktivitas yang sangat baik sehingga perlu dilakukan pengecilan ukuran menjadi nano material untuk dapat dimanfaatkan dan meningkatkan sifat dari MnO. Karakterisasi fasa dan morfologi serbuk Manganese Oxide (MnO) bertujuan untuk memperkecil ukuran butir MnO dari ukuran mikro menjadi ukuran nano menggunakan metode sol-gel dengan variasi waktu sintering. Sol-gel merupakan metode sintesis yang sederhana dan sudah teruji dalam mensintesiskan berbagai macam material oksida berukuran mikro menjadi nano. Sintering time merupakan teknik yang dilakukan dalam proses sintesis untuk mengeringkan material dengan suhu diatas suhu normal. Suhu yang digunakan dalam proses sintering dimulai dari suhu 600 C hingga 1000 C. Material uji yang digunakan dalam penelitian ini adalah manganese oxide (MnO). MnO yang dipilih berbentuk serbuk berukuran mikro dengan unsur Mn sebesar 89 72 Wt% dan O sebesar 10 29 Wt% merupakan inovasi baru untuk menghasilkan material oksida berukuran nano dimana proses yang lazim digunakan dalam proses sol-gel menggunakan solvent ehtylene glycol dengan material oksida campuran untuk menghasilkan material oksida. XRD merupakan pengujian untuk mengetahui karakterisasi fasa dari suatu material SEM merupakan pengujian untuk mengetahui karakterisasi morfologi EDX merupakan pengujian untuk mengetahui karakterisasi kandungan unsur dari suatu material dan FTIR merupakan pengujian untuk mengetahui karakterisasi dari gugus oksida suatu material. Temperatur sintering yang digunakan dalam penelitian ini sebesar 600 C dengan variasi waktu 30 menit 60 menit dan 90 menit. Hasil karakterisasi fasa dari XRD diperoleh ukuran kristal serbuk MnO yang terkecil dengan sintering 30 menit yang berukuran kristal sebesar 47.3 nm. Intensitas (derajat kristalinitas) tertinggi terjadi pada MnO dengan waktu sinter 90 menit. Hasil karakterisasi morfologi dari SEM menunjukkan perubahan morfologi MnO dari butir berbentuk segitiga mikron meter menjadi butir berbentuk bulat nanometer. Hasil karakterisasi unsur dari EDX menunjukkan perubahan Unsur Mn yang terendah dan O tertinggi ditunjukkan pada MnO 30 menit. Hasil karakterisasi gugus dari FTIR menunjukkan pergeseran C-H dan Mn-O diikuti dengan meningkatnya gugus N-H C O dan Mn-O. 8195 ABSTRACT Sasongko Muhammad Ilman Nur. 2017. Phase and Morphology Characterization of Nano Powder Manganese Oxide (MnO) With Variations Sintering Time. Thesis Mechanical Engineering Department Faculty of Engineering State University of Malang. Advisors (1) Rr. Poppy Puspitasari S.Pd. M.T. Ph.D. (2) Widiyanti. Hj. Dr. M.Pd. Keywords Phase Manganese Oxide MnO Morphology Sintesis Sol-gel Sintering time Manganese oxide (MnO) contained in one of the many rock types and may take the form of minerals. MnO has its drawbacks namely highly reactive oxidizing species classified as dangerous and can explode if they are at a temperature above 55 C. But MnO have magnetic properties electrochemical properties and excellent conductivity properties so that should be downsizing into a nano-material to be used and improve the properties of MnO. Phase and morphology characterization of powder Manganese Oxide (MnO) aims to reduce the grain size of the MnO micro size to a size of nano using sol-gel method with sintering time variations. Sol-gel is a synthesis method is simple and has been tested for synthesizing a wide variety of micro-sized oxide materials into nano. Sintering time is a technique performed in the synthesis process to dry the material to a temperature above normal temperature. The temperature used in the sintering process starting from a temperature of 600 C to 1000 C. Material samples used in this study is manganese oxide (MnO). MnO selected micro-sized powder form with elements of Mn and O 89.72 Wt% Wt% at 10.29 is a new innovation to produce nano-sized oxide materials which process commonly used in the sol-gel process using solvent ehtylene glycol with the mixed oxide material to produce oxide materials. XRD is a test to determine the phase of a material characterization SEM is a test to determine the morphological characterization EDX is a test to determine the content of the element characterization of a material and FTIR is a test to determine the characterization of clusters oxide material. Sintering temperature used in this study of 600 C with a variation of 30 minutes 60 minutes and 90 minutes. The characterization results of XRD phase obtained crystal size of the smallest MNO powders by sintering 30 minutes crystal size of 47.3 nm. Intensity (degree of crystallinity) is highest in MnO with sinter time of 90 minutes. The results of the morphological characterization of SEM showed morphological changes of grain MnO micron meter triangular shaped into spherical grains nanometers. The characterization results indicate a change elements of EDX element of the lowest Mn and O supreme shown in MnO 30 minutes. The results of cluster characterization of FTIR showed a shift in the C-H and Mn-O followed by increased group N-H C O and Mn-O.
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | ?? ?? |
| Divisions: | Fakultas Teknik (FT) > Departemen Teknik Mesin (TM) > S1 Pendidikan Teknik Mesin |
| Depositing User: | Users 2 not found. |
| Date Deposited: | 09 May 2017 04:29 |
| Last Modified: | 09 Sep 2017 03:00 |
| URI: | http://repository.um.ac.id/id/eprint/42633 |
Actions (login required)
 |
View Item |